Izod Impact (Unnotched) ASTM D4812, ISO 180

Scope:
Unnotched Izod Impact is a single point test that measures a materials resistance to impact from a swinging pendulum. Izod impact is defined as the kinetic energy needed to initiate fracture and continue the fracture until the specimen is broken. This test can be used as a quick and easy quality control check to determine if a material meets specific impact properties or to compare materials for general toughness.

Test Procedure:
The specimen is clamped into the pendulum impact test fixture with the thin edge facing the striking edge of the pendulum. The pendulum is released and allowed to strike through the specimen. If breakage does not occur, a heavier hammer is used until failure occurs.

Specimen size:
The standard specimen for ASTM is 64 x 12.7 x 3.2 mm (2½ x ½ x 1/8 inch). The most common specimen thickness is 3.2 mm (0.125 inch), but the preferred thickness is 6.4 mm (0.25 inch) because it is not as likely to bend or crush.

The standard specimen for ISO is a Type 1A multipurpose specimen with the end tabs cut off. The resulting test sample measures 80 x 10 x 4 mm.

Data:
ASTM impact energy is expressed in J/m or ft-lb/in. Impact strength is calculated by dividing impact energy in J (or ft-lb) by the thickness of the specimen. The test result is typically the average of 5 specimens.

ISO impact strength is expressed in kJ/m2. Impact strength is calculated by dividing impact energy in J by the area under the notch. The test result is typically the average of 10 specimens.

The higher the resulting numbers the tougher the material. 